Resumen
NOHELYA JUNES PRADO, Luisa Stephanie; CABALLERO GARCIA, Stefany; BARRAGAN SALAZAR, Carolina y GONZALES SOTO, Néstor. Coronal microleakage according to the temporary restorative materials used in endodontic treatment. Rev Cubana Estomatol [online]. 2020, vol.57, n.2 Epub 13-Jul-2020. ISSN 1561-297X.
Introduction:
Coronal microleakage caused by temporary restorative materials is viewed as one of the reasons for endodontic failure. Efforts have been made in recent years to create a temporary restorative material capable of preventing that problem.
Objective:
Compare in vitro coronal microleakage of an "experimental cement" and four temporary restorative materials used in endodontics.
Methods:
Class I cavities were made in 90 premolar teeth divided into 10 groups (n= 9) and evaluated at two time periods (1 and 2 weeks). The "experimental cement" was prepared and then coronal sealing of the teeth was performed with the experimental Cement, F (VOCO), Eugenato (MOYCO), Ketac™ Molar Easymix 3M (ESPE) and Coltosol® F. The pieces were submerged in India ink (Pelikan)for 1 and 2 weeks. Microleakage was evaluated on the interface dentin wall / temporary restoration using a stereo microscope (Leica Microsystems LAS EZ version 2.0.0). Measurement was made in millimeters using the software LAS EZ version 2.0.0.
Results:
Statistically significant differences were found (p< 0.05) when comparing coronal microleakage in the five temporary restorative materials according to exposure time in ink (1 and 2 weeks).
Conclusions:
The experimental cement had less microleakage than Coltosol® F and Ketac™ Molar EasyMix 3M (ESPE). However, none of the four materials was capable of completely preventing microleakage.
Palabras clave : endodontics; dental leakage; temporary restorative materials.