vol.18 número3Análisis para la modelación y optimización geométrica de un reactor tipo tornillo sin-fin empleando el método de grafos dicromáticosEvaluación del impacto de los procesos intermedios de la producción de acero en la cogeneración de electricidad de la industria siderúrgica índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

  • No hay articulos citadosCitado por SciELO

Links relacionados

  • No hay articulos similaresSimilares en SciELO

Compartir


Ingeniería Mecánica

versión On-line ISSN 1815-5944

Resumen

DIAZ-BATISTA, Daniel; DIAZ-FORCELLEDO, Daniel; MAZORRA-MESTRE, Marta  y  VALIN-RIVERA, José-Luis. Mechanical behavior of Cuban henequen fibers and interphase with thermoplastic polymers of the polyolefin family. Ingeniería Mecánica [online]. 2015, vol.18, n.3, pp.148-157. ISSN 1815-5944.

Incorporating fibers from agave fourcroydes, also named henequen, grown in Cuban farm conditions, into thermoplastic-matrix compositedesign took evaluating mechanical behavior of both the fiber and interphase with polymeric matrix candidates. Fibers from Limonar area in the province of Matanzas were tested, finding 500 MPa as typical tensile strength value. Statistical of fiber cross sectional area and perimeter to cross sectional area ratio is also showed. Fiber interaction with low density polyethylene yielded an interphase shear strength equal to 5.6 MPa but increased to 8.4 interacting with ethylene 1-hexene copolymer. For these experimental conditions, critical lengths of 8.1 millimeters and shorter were obtained. Are also presented both, an alternative to prepare pull-out test specimens and a device to evaluate them in a universal tensile testing machine.

Palabras clave : henequen; thermoplastic polymer; lignocellulosic fiber; interphase; pull-out test; composite material.